steel grade:
XM-12
UNS S15500
XM-12 / S15500 Chemical composition
| Carbon | 0.07 max |
| Chromium | 14 - 15.5 |
| Copper | 2.5 - 4.5 |
| Iron | Balance |
| Manganese | 1 max |
| Nickel | 3.5 - 5.5 |
| Niobium | 0.15 - 0.45 |
| Phosphorus | 0.04 max |
| Silicon | 1 max |
| Sulphur | 0.03 max |
The alloy XM-12 / S15500 combines good strength, transverse toughness and ductility, hardness capability and corrosion resistance compared with 304 stainless. It may be used in the solution treated condition or heat treated to obtain a wide variety of properties.
15Cr-5Ni is a martensitic precipitation hardening stainless steel offering high strength and hardness along with excellent corrosion resistance. Generally similar to Custom 630 (17Cr-4Ni) in composition and properties, 15Cr-5Ni is chemically balanced to eliminate all but trace amounts of delta ferrite, thus providing superior transverse toughness and ductility plus a higher degree of forgeability.
XM-12 stainless steel
APPLICATION of XM-12 / S15500
Aircraft components, fabricated parts in high pressure corrosive environments including valves, shafts, fasteners, fittings and gears
XM-12 mechanical properties:
| |
Tensile strength Rm （MPa） |
Yield strength Rp0.2 （MPa）min |
Elongation A （%）min |
Reduction of area Z （%）min |
Charpy AKv min |
Hardness HBW |
| H900 | 1310 | 1170 | 10 | 35 | 388 | |
| H1025 | 1070 | 1000 | 12 | 35 | 331 | |
| H1075 | 1000 | 860 | 13 | 45 | 331 | |
| H1100 | 965 | 795 | 14 | 45 | 302 | |
| H1150 | 930 | 725 | 16 | 50 | 277 |
XM-12 / S15500 Specifications：
steel round bar : dia 2mm to 1000mm
Square-shape steel: 50mm to 600mm
Steel sheet: thickness 0.5mm-12mm width 1000mm max
Steel strip: thickness 0.5mm-4mm width 300mm max
steel plate : thickness 5mm-800mm Width: 10mm to 1000mm
steel pipe: OD 8-800mm
Length: random length/ fixed length
Delivery condition: hot forged / hot rolled /cold-rolled
annealing/normalizing + tempering/quenching + tempering/ solution
Surface : black/ground/rough turned/fine machining/Peeled / mill-fimish surface
metallurgical processing: electrode arc + LF/VD/VOD/ESR/ VIM/ VAR
Ultrasonic inspection: 100% ultrasonic test